| 摘要 |
Pyrogenically prepared, doped zinc oxide powder, wherein the doping component comprises at least one oxide from the group aluminum, gallium, indium, germanium, tin and is present in the doped zinc oxide powder in an amount of from 0.005 to 15 wt. %, and wherein the doped zinc oxide powder is in the form of aggregates of primary particles having a mean maximum diameter of from 30 to 400 nm. It is prepared by oxidation from zinc powder and at least one doping agent, wherein the process zones vaporisation, nucleation, oxidation and quenching are passed through and the doping agent is metered in in the nucleation zone, in which the temperature is below the boiling temperature of zinc. The doped zinc oxide powder can be used in electrically conductive lacquers and coatings.
|