The present invention discloses a high strength low shrinkage polyester drawn yarn used as industrial yarns and a process or producing the same. The strength low shrinkage polyester drawn yarn has a thermal relaxation stress change ratio of 5 to 100% and a thermal relaxation stress area ratio of 50 to 140% on a thermal relaxation and shrinkage stress curve with a final temperature set to 170° C. The process for producing a high strength low shrinkage polyester drawn yam by a direct spin draw (DSD) process in which a quenching delay region I is mounted, wherein the high strength low shrinkage polyester drawn yarn is produced in such methods that a spinning oil is attached to the yarn being spun with an oiling apparatus 8 mounted at the position 500 to 1,500 mm below from the lower bottom surface of the insulating board 3 , the relaxation stress of the yarn is controlled with one or tow tension guides 9 mounted between Godet rollers of a relaxation region III, or both oiling apparatus 8 and tension guides 9 are mounted.
|