| 摘要 |
<P>L'INVENTION A TRAIT AU DOMAINE DES CERAMIQUES.</P><P>ELLE CONCERNE UNE CERAMIQUE A BASE DE ZIRCONE ESSENTIELLEMENT FORMEE D'AU MOINS 40 EN POIDS DE ZIRCONE PARTIELLEMENT STABILISEE DU SYSTEME ZRO-YO-CEO, DONT LA PROPORTION DES COMPOSANTS SE SITUE DANS LA PLAGE DEFINIE PAR LA LIGNE JOIGNANT LES POINTS A, B, C, D ET E D'UN DIAGRAMME TERNAIRE DONT LES SOMMETS SONT DONNES PAR ZRO, YO ET CEO, EN MOLES : A (87,5, 12, 0,5), B (95,5, 4, 0,5), C (95,5, 2, 2,5), D (92,5, 0,5, 7,0), ET E (85, 0,5, 14,5) ET 3 A 60 EN POIDS DE ALO, ET A UN DIAMETRE MOYEN DES CRISTAUX NE DEPASSANT PAS 2MM ET UNE RESISTANCE A LA FLEXION D'AUMOINS 981 MPA, LA STRUCTURE DES CRISTAUX ETANT TETRAGONALE A 50 EN VOLUME AU MOINS ET MONOCLINIQUE A 30 EN VOLUME AU PLUS, APRES 10 HEURES DANS LA VAPEUR D'EAU A 180C ET 1 MPA.</P><P>LA CERAMIQUE DE L'INVENTION SE CARACTERISE PAR SA GRANDE RESISTANCE MECANIQUE ET SA GRANDE TENACITE AINSI QUE PAR SA STABILITE THERMIQUE ET HYDROTHERMIQUE.</P> |