The invention is directed to a glass composition that can be used to make glass frits suitable for use in the manufacturing of microreactors. The glass compositions, after final sintering to produce a finished microreactor, have a surface crystalline layer of 30 mum or less, or are completely amorphous throughout. Generally, the borosilicate glasses of the invention have a composition of B<SUB>2</SUB>O<SUB>3</SUB>=12-22 mol %; SiO<SUB>2</SUB>=68-80 mol % and additional components selected from the group consisting of either (a) Al<SUB>2</SUB>O<SUB>3</SUB>=3-8 mol % and Li<SUB>2</SUB>O=1-8 mol %, or (b) K<SUB>2</SUB>O=0-2 mol % and Na<SUB>2</SUB>O=0-2 mol %, except that both K<SUB>2</SUB>O and Na<SUB>2</SUB>O cannot both equal zero at the same time. One borosilicate glass has a composition, in mole percent (mol %) of B<SUB>2</SUB>O<SUB>3</SUB>=18-22 mol %, SiO<SUB>2</SUB>=75-80 mol %, K<SUB>2</SUB>O=0-2 mol %, and Na<SUB>2</SUB>O=0-2 mol %, except that both K<SUB>2</SUB>O and Na<SUB>2</SUB>O cannot both equal zero at the same time.
|