Disclosed herein is a precipitation hardening cold-rolled steel sheet and method for manufacturing the same, which can be used for structural components such as seat rails and the like of a vehicle body. The steel sheet comprises, by weight %, C: 0.07˜0.1%, Mn: 1.4˜1.7%, P: 0.05˜0.07%, S: 0.005% or less, acid-soluble Al: 0.1˜0.15%, Nb: 0.06˜0.09%, B: 0.0008˜0.0012%, Sb: 0.02˜0.06%, and the balance of Fe and other unavoidable impurities. The steel sheet has a yield strength of 750 MPa or more and a yield ratio of 85% or more, and is free from surface defects due to a very low degree of oxide enrichment on the surface thereof. |