| 摘要 |
PROBLEM TO BE SOLVED: To provide a curing sheet superior in strength and tearing strength, with extremely little deterioration in flame retardant performance while in practical use. SOLUTION: This curing sheet is characterized by using a polyamide multi-filament having single-thread fineness of 1.5 to 100 dtex, having strength of 4.6 to 10 cN/dtex and including 0.1 to 10 wt.% of a triazine-based compound. The content of the triazine-based compound is set to 0.1 to 1.9 wt.%, and a maximum particle size of the triazine-based compound is set to 10μm or less, and an average particle size is desirably set to 0.1 to 5μm, and a copper compound is further desirably included in this polyamide multi-filament. COPYRIGHT: (C)2007,JPO&INPIT
|