| 摘要 |
A method of making cemented carbide at which powders forming hard constituents and powders forming binder phase are wet milled together with a pressing agent is disclosed. The slurry is dried, preferably by spray drying, compacted into bodies of desired shape and sintered. A cemented carbide powder with a reduced compacting pressure at a predetermined weighing in of 18% shrinkage can be obtained by using from about 1 to about 3 wt-% pressing agent with the following composition: less than about 90 wt-% PEG and greater than about 10 wt-% of long chain C>=20 fatty acids, their esters and salts, in particular, erucic acid and/or behenic acid. The invention also relates to a cemented carbide powder with low compaction pressure.
|