CROSS-LINKED THERMOPLASTIC POLYURETHANE/POLYUREA AND METHOD OF MAKING SAME

摘要

A cross-linked thermoplastic polyurea is formed by heating a mixture containing a thermoplastic urethane base material, a monomeric and/or polymeric di-isocyanate comprising between 1 to 10% of the total weight of the mixture, and a diamine comprising between 1 to 10% of the total weight of the mixture. A thermoplastic polyurethane may be formed by substituting hydroquinone for the diamine. The mixture is heated to a temperature within the range of 250 °F to 550 °F. The heated mixture, which is flowable, is then injected into an injection molding device. The mixture is then cured at a temperature between 150 °F to 250 °F for a period of time between 2 and 36 hours. The cross-linked thermoplastic polyurethane/polyurea retains the excellent flowability characteristics of a thermoplastic urethane while the same time exhibits good abrasion, tensile strength, rebound, and compression set characteristics which are similar to those found in thermoset urethanes.