| 摘要 |
<p>The invention relates to a polymer mixture, which is based on (Meth)acrylate (co)polymer components a), b), c, and/or d) in accordance with Claim 1, wherein a test body produced from said polymer mixture also has the following properties: I. A tensile module (ISO 527) of at least 2600 Mpa; II. a vicat softening temperature VST (ISO 306-B50) of at least 109 degree C; III an impact strength (ISO 179-2D, flatwise) of at least 17 Kj/m2 and IV. A melting index MVR (ISO 1133, 230 degree C / 3.8 kg) of at least 1.5 cm3/10. The invention also relates to injection molded bodies and to the utilization of said polymer mixture for the production of injection molded parts.</p> |