| 摘要 |
<p>The invention is directed to a polypropylene resin, which is suitable for manufacturing an air quenched blown film. The resin has a melt flow rate of greater than 5 g/10 min, less than 2% xylene solubles, a pentad isotacticity of greater than 95%, an isotactic pentad/triad ratio of greater than 95%, a crystallinity of at least 65%, and a crystallization temperature of at least 127 degree C. The polypropylene resin contains from 500 ppm to 2500 ppm of a nucleator/clarifier additive. A quenched blown film made from resin exhibits a crystallization onset temperature of at least 116 degree C and a crystallization half-life time of less 4.1 seconds or less when tested using fast DSC analysis with a scan rate of 200 degree C/minute.</p> |