PROBLEM TO BE SOLVED: To provide a polyarylene sulfide resin composition remarkably reduced in occurrence of corrosive gas in molding, having little occurrence of burr and improved in a crystallization rate. SOLUTION: The resin composition is obtained by formulating (A) 100 pts.wt. polyarylene sulfide resin having 10-500 Pa s melting viscosity (at 310°C and 1,200 sec<SP>-1</SP>shearing rate) with (B) 0.05-1.2 pts.wt. carbon nano tube having 5-100 nm average diameter and 50-2,000 aspect ratio and (C) 0-250 pts.wt. inorganic filler. COPYRIGHT: (C)2006,JPO&NCIPI
|