HOCHFESTE HEISSTAUCHZINKBESCHICHTETE STAHLPLATTE MIT HERVORRAGENDEN DUKTILITÄTSEIGENSCHAFTEN UND VERFAHREN ZU DEREN HERSTELLUNG

摘要

A steel sheet having a composition comprising C: 0.05-0.20 mass %, Si: 0.3-1.8 mass %, Mn: 1.0-3.0 mass %, Fe of the balance and inevitable impurities is subjected to a primary step of primary heat treatment and subsequent rapid cooling to Ms point or lower, a secondary step of secondary heat treatment and subsequent rapid cooling, and a tertiary step of galvanizing treatment and rapid cooling, so as to turn the structure of the steel sheet into a composite structure of 20% or more by volume of tempered martensite, 2% or more by volume of retained austenite, ferrite and a low-temperature transformation phase. A galvanized layer is deposited on the surface of the steel sheet. It is preferred to cool the steel sheet to 300 DEG C at a cooling rate of 5 DEG C/sec. or more after the galvanizing treatment. After the galvanizing treatment, alloying treatment may be conducted.