Geschweisstes Stahlrohr zum Hydroformen und Verfahren zu seiner Herstellung
摘要
A welded steel pipe is formed by heating or soaking an untreated welded steel pipe having a steel composition containing, on the basis of mass percent: about 0.05% to about 0.2% C; about 0.2% or less of Si; about 1.5% or less of Mn; about 0.1% or less of P; about 0.01% or less of S; about 0.1% or less of Al; and about 0.01% or less of N; and by reduction-rolling the treated steel pipe at a cumulative reduction rate of at least about 35% and a final rolling temperature of about 500 DEG C to about 900 DEG C. The welded steel pipe exhibits excellent hydroformability, i.e., has a tensile strength of at least about 400 MPa and an nxr product of at least about 0.22. The treated steel pipe is preferably reduction-rolled at a cumulative reduction rate of at least about 20% below the Ar3 transformation point. The welded steel pipe is suitable for forming structural components. <IMAGE>