WARM-, KALTGEWALZTE UND SCHMELZ-GALVANISIERTE STAHLPLATTE MIT EXZELLENTEM RECKALTERUNGSVERHALTEN |
摘要 |
The present invention provides a steel sheet having a chemical composition comprising 0.15% or less C, 2.0% or less Si, 3.0% or less Mn, P, S, Al and N in adjusted amounts, from 0.5 to 3.0% Cu, or one or more of Cr, Mo and W in a total amount of 2.0% or less, and having a composite structure comprising ferrite and martensite having an area ratio of 2% or more. The steel sheet is in the form of a high-strength hot-rolled steel sheet, a high-strength cold-rolled steel sheet, or a hot-dip galvanized steel sheet. There is thus available a steel sheet excellent in press-formability and in strain age hardening property as represented by a DELTA TS of 80 MPa or more. <IMAGE> |
申请公布号 |
DE60116477(D1) |
申请公布日期 |
2006.03.30 |
申请号 |
DE2001616477 |
申请日期 |
2001.03.30 |
申请人 |
JFE STEEL CORP., TOKIO/TOKYO |
发明人 |
MATSUOKA, MIZUSHIMA WORKS;SHIMIZU, MIZUSHIMA WORKS;SAKATA, TECHNICAL RESEARCH LABORATORIES;FURUKIMI, OSAMU |
分类号 |
C22C38/00;C21D1/02;C21D1/18;C21D7/13;C21D8/02;C21D9/46;C22C38/02;C22C38/04;C22C38/06;C22C38/12;C22C38/16;C23C2/02;C23C2/06;C23C2/28;C23C2/40 |
主分类号 |
C22C38/00 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|