| 摘要 |
Disclosed is a wear-resistant sintered aluminum alloy with high strength and a manufacturing method thereof. The sintered aluminum alloy contains, by mass: 3.0-10% zinc; 0.5-5.0% magnesium; 0.5-5.0% copper; 0.1-10% hard particles; impurities; and aluminum. The metallographic structure has an aluminum alloy matrix in which the hard particles dispersed; and an intermetallic compound phase being dispersedly precipitated in the aluminum alloy matrix. Using an aluminum powder, a hard particles powder and other powders, a compact is formed and sintered at 580-610 degrees C., then cooled and subjected to heat treatment at a temperature of 460-490 degrees C., including water-quenching and aging at 110-200 degrees C.
|