发明名称 |
Dissimilar material weld joint formed by joining iron type material and aluminum type material, and weld joining method |
摘要 |
Disclosed are: a dissimilar material weld joint being formed by joining an iron type material and an aluminum type material and having not only a high strength but also an excellent ductility; and a weld joining method allowing such a joint to be stably produced. A dissimilar material weld joint 1 formed by joining an iron type material 2 and an aluminum type material 3 , wherein: voids 4 a are formed beforehand on the side of said iron type material 2 at a predetermined interval along a weld line 6 ; both said iron type and aluminum type materials are weld joined so that said voids 4 a are filled with molten aluminum 7 ; and the minimum value of the ratio (L-Al)/(L-Fe) of the length (L-Al) of an aluminum type welding material 10 with which said voids 4 a are filled to the length (L-Fe) of said iron type material 2 adjacent to said voids 4 a filled with said aluminum type welding material 10 along said weld line 6 on the section containing said weld line 6 is in the range from 0.5 to 7, both the lengths (L-Al) and (L-Fe) being the lengths per 100 mm in length of the weld line 6 formed after welding.
|
申请公布号 |
US2005274776(A1) |
申请公布日期 |
2005.12.15 |
申请号 |
US20050147241 |
申请日期 |
2005.06.08 |
申请人 |
KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) |
发明人 |
TAKEDA MIKAKO;MATSUMOTO KATSUSHI;KINEFUCHI MASAO;NAKAGAWA TOMOKAZU;FUKUMOTO KOJI;TAKEDA HIROYUKI;MURAI YASUO |
分类号 |
B23K9/23;B23K26/32;B23K33/00;(IPC1-7):B23K35/24;B23K1/19;B23K20/16 |
主分类号 |
B23K9/23 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|