Method of forming Ti 6-2-4-2 sheet with enhanced cold-formability |
摘要 |
Systems and methods for enhancing the cold-formability of Ti 6-2-4-2 sheet material are described herein. Embodiments of these methods comprise coldforming a predetermined, pretreated Ti 6-2-4-2 alloy into a cold-formed shape; subjecting the cold-formed shape to a post-forming annealing cycle comprising: heating the cold-formed shape to about 1450 +/- 25 DEG F (788 +/- 14 DEG C); holding the cold-formed shape at about 1450 +/- 25 DEG F (788 +/- 14 DEG C) for about 15 +/- 2 minutes; and cooling the cold-formed shape to room temperature. Embodiments of these methods further comprise subjecting the predetermined Ti 6-2-4-2 alloy to a pre-forming annealing cycle comprising: heating the predetermined alloy to a pre-forming annealing temperature of about 1550-1750 (843-954 DEG C) DEG F; holding the predetermined alloy at the pre-forming annealing temperature for about 30 minutes; and cooling the predetermined alloy to room temperature. These methods allow components comprising 90 DEG bend angles, having a bend factor as low as about 6.2 T, to be achieved. <IMAGE>
|
申请公布号 |
EP1598438(A1) |
申请公布日期 |
2005.11.23 |
申请号 |
EP20050251624 |
申请日期 |
2005.03.17 |
申请人 |
UNITED TECHNOLOGIES CORPORATION |
发明人 |
HANSEN, JAMES OLAF;ANDERSON, DAVID WILLIAM |
分类号 |
F01D5/28;B21D22/02;C22C14/00;C22F1/00;C22F1/18;F02C7/00;(IPC1-7):C22F1/18 |
主分类号 |
F01D5/28 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|