| 摘要 |
A method of making aluminum alloy sheet in a continuous in-line process is provided. A continuously-cast aluminum alloy strip is optionally quenched, hot or warm rolled, annealed or heat-treated in-line, optionally quenched, and preferably coiled, with additional hot, warm or cold rolling steps as needed to reach the desired gauge. The process can be used to make aluminum alloy sheet of T or O temper having the desired properties, in a much shorter processing time. The T or O temper may be selected by annealing the strip to achieve an O temper or solution heat treating the strip to achieve a T temper, and, if a T temper is desired, quenching the strip subsequent to the solution heat treating. The invention further provides a hot or warm rolling step wherein the strip is substantially reduces to a final thickness about 10-65% from a casting thickness.
|