LONG FIBER-REINFORCED POLYLACTIC ACID-BASED RESIN COMPOSITION AND METHOD FOR PRODUCING THE SAME |
摘要 |
PROBLEM TO BE SOLVED: To obtain a long fiber-reinforced polylactic acid-based resin composition for providing a biodegradable plastic molding having mechanical strength and heat resistance (high deflection temperature under load) and to provide a method for producing the same. SOLUTION: The long fiber-reinforced polylactic acid-based resin composition comprises a polylactic acid-based resin, a reinforced fiber having substantially≥2 mm fiber length and talc having 0.1-3μm average particle diameter in which the amount of the reinforced fiber is 5-70 mass% in the composition, the amount of the talc is 5-25 mass% in the composition and the reinforced fiber is treated with a sizing agent containing a urethane resin and having≤20 mass% epoxy resin content. The continuous material of a reinforced fiber bundle treated with the sizing agent containing a urethane resin and having≤20 mass% epoxy resin content is impregnated with a melt comprising the polylactic acid-based resin and 5.5-33 parts by mass of talc having 0.1-3μm average particle diameter based on 100 parts by mass of the polylactic acid-based resin to give the composition containing 5-70 mass% of the reinforced fiber. COPYRIGHT: (C)2005,JPO&NCIPI
|
申请公布号 |
JP2005220177(A) |
申请公布日期 |
2005.08.18 |
申请号 |
JP20040027322 |
申请日期 |
2004.02.03 |
申请人 |
ASAHI FIBER GLASS CO LTD |
发明人 |
HIGASHIYAMA HIDEYUKI;MATSUBARA TAKAYUKI;MASUJIMA KENICHIRO |
分类号 |
C08J5/06;C08K3/34;C08K9/08;C08L67/04;C08L101/16;(IPC1-7):C08L67/04 |
主分类号 |
C08J5/06 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|