Thick-section metal forming via friction stir processing

摘要

Friction stir processing (FSP) modifies the surface microstructure of metals so that thick-section metal workpieces can be bent over large angles without formation of surface cracks. A thick 2519-T8 aluminum plate (25.4 mm thick and 50.8 mm wide) was friction stir processed across the pre-tensile surface to a depth of 6.3 mm, and was then bent at room temperature over a punch with radius 38.1 mm into a v-shaped die to an 80° bend angle. Whereas unprocessed workpieces of this type exhibited surface cracking at 31° bend angle and failed at 40° bend angle, no cracking was evident for the friction stir processed workpiece up to 80° bend angle.