| 摘要 |
PROBLEM TO BE SOLVED: To provide a steel sheet with a low yield ratio, high strength and high toughness, which does not increase a material cost through adding a large amount of alloy elements or the like, does not deteriorate the toughness of a weld heat-affected zone, and is manufactured at high manufacturing efficiency and at a low cost; and to provide a manufacturing method therefor. SOLUTION: The steel sheet with the low yield ratio, high strength and high toughness comprises, by mass%, 0.03-0.1% C, 0.01-0.5% Si, 1.2-2.5% Mn, 0.05-0.4% Mo, 0.005-0.04% Ti, 0.08% or less Al, while controlling C/(Mo+Ti) to 1.2 to 3.0, and the balance substantially Fe; and has a metallographic structure of a three-phase structure consisting substantially of ferrite, bainite and island martensite, in which an area fraction of the island martensite is 3 to 20%. The steel sheet preferably further includes, by mass%, 0.005-0.07% Nb and/or 0.005-0.1% V, and controls C/(Mo+Ti+Nb+V) to 1.2 to 3.0. COPYRIGHT: (C)2005,JPO&NCIPI
|