| 摘要 |
To provide a powder coating composition being capable of forming a coating film which has good pigment dispersibility, is excellent in weather resistance, film forming ability, appearance and stain-proofing property and, when used for PCM, is difficult to cause cracks because of its particularly excellent bending resistance at the time of bending of a metal plate. The powder coating composition comprises a powder which contains 100 parts by weight of a vinylidene fluoride copolymer having a melting point of not higher than 150 DEG C, a crystallinity of not higher than 35 % and a weight average molecular weight (Mw) of 1 x 10<4> to 5 x 10<5> and 10 to 400 parts by weight of a methyl methacrylate copolymer having a glass transition temperature of not higher than 110 DEG C and a weight average molecular weight of 1 x 10<4> to 5 x 10<5>; an average particle size of particles constituting the powder being from 1 to 100 mu m and an apparent density of the powder being from 0.2 to 1 g/ml. |