Disclosed is a polypropylene molding material obtainable by the reaction of a crystalline polypropylene resin and a peroxide, said polypropylene molding material having (A) a melt flow rate of 20 to 100 g/10 min and a weight average molecular weight to number average molecular weight ratio of 1.5 to 3.5 as measured by gel-permeation chromatography, (B) a content of hydrocarbons having 20 to 70 carbon atoms of 0.05% by weight or less, (C) a mean elution temperature (T50) of 75 to 120 DEG C and a degree of variation of elution ( sigma ) of 9 or smaller, and (D) a Q2/Q1 ratio of 0.75 to 0.95, wherein Q1 is a weight average molecular weight to number average molecular weight ratio of said crystalline polypropylene resin as measured by gel-permeation chromatography, and Q2 is a weight average molecular weight to number average molecular weight ratio of said propylene molding material as measured by gel-permeation chromatography. |