| 摘要 |
<p><P>PROBLEM TO BE SOLVED: To provide a method for manufacturing a glass plate having a single layer low reflective film, the glass plate which is coated with a silicon oxide film and whose visible light reflectance is made small by controlling the refractive index of the silicon oxide film by firing conditions, the silicon oxide film being excellent in durability such as wear resistance or chemical resistance and having high hardness at an arbitrary thickness. <P>SOLUTION: The method for manufacturing the glass plate having the low reflective film comprises applying a treating liquid obtained by blending an organic silicon compound (A), a binder resin being thermally decomposed at 40-270°C (B), and an organic solvent (C) on the surface of a transparent glass substrate, then drying the obtained coated film, and firing the glass substrate having the coated film at 400-800°C so that the porosity of the coated film becomes 15-25% after firing. <P>COPYRIGHT: (C)2005,JPO&NCIPI</p> |