The present invention relates to glass, glass-ceramic materials, lamp reflectors and processes for making them. The glass material has a composition, by weight of the total composition, comprising 56-67% SiO2; 9-22% Al2O3; 3.4-3.8% Li2O; 1.8-2.6% ZnO; 1.5-2.5% MgO; 3.3-5% TiO2; 0-2.5% ZrO2; 1.5-3% B2O3; 0-6% P2O5; 0-0.6% F; less than 500 ppm Fe; and components resulting from effective amount of at least one refining agent. The glass-ceramic material of the present invention contains beta-quartz solid solution as the predominant crystalline phase, and can be obtained by proper thermal treatment of the glass-ceramic material. The glass-ceramic material is particularly suitable for heat-resistant lamp reflectors which require a high surface smoothness Ra of lower than 75 nm, a low CTE between 25 and 300° C. of less than 10x10<-7 >K<-1>, and IR transmission at about 1050 nm of over 80% at a thickness of 3 mm.
|