摘要 |
A porous catalyst support having an increased average pore size is produced from a mixed metal oxide material. In accordance with one embodiment, a method for preparing a mixed metal oxide material includes providing a mixed metal oxide precursor containing at least two metals, calcining the mixed metal oxide precursor at a temperature sufficient to form a thermally and mechanically stable mixed metal oxide material, and leaching the mixed metal oxide material in a leach solution with a constituent that dissolves one metal oxide. Preferably, the calcination temperature is approximately between 300°C and 1300°C. The leaching constituent may be chosen from the group including acidic solutions of HCl, HNO3, H2SO4, H3PO3, and their combinations, or basic solutions of NH3, NaOH, KOH, and their combinations. |