摘要 |
本发明涉及一种高强度Al<SUB>2</SUB>O<SUB>3</SUB>/ZrO<SUB>2</SUB>(2Y)/LaAl<SUB>11</SUB>O<SUB>18</SUB>复相陶瓷及制备方法,属于精细化工领域。本发明的主要特征在于以La、Zr、Y、Al的无机盐和α-Al<SUB>2</SUB>O<SUB>3</SUB>为原料,首先通过沉淀包裹工艺制备或Al<SUB>2</SUB>O<SUB>3</SUB>、ZrO<SUB>2</SUB>(2Y)和氧化锆包裹的氧化铝的复相粉体,然而高温烧结成Al<SUB>2</SUB>O<SUB>3</SUB>/ZrO<SUB>2</SUB>(2Y)/LaAl<SUB>11</SUB>O<SUB>18</SUB>复相陶瓷。该材料的突出特点是,瓷体中ZrO<SUB>2</SUB>(2Y)和LaAl<SUB>11</SUB>O<SUB>18</SUB>的含量总和为30vol%,其中板状LaAl<SUB>11</SUB>O<SUB>18</SUB>颗粒在烧结过程中通过Al<SUB>2</SUB>O<SUB>3</SUB>和La<SUB>2</SUB>O<SUB>3</SUB>间的原位反应生成,瓷体显微结构均匀,在较宽的烧结温度范围内均表现出良好的力学性能好,适用于工业化批量生产。所提供的复相陶瓷Al<SUB>2</SUB>O<SUB>3</SUB>的含量为70vol%,ZrO<SUB>2</SUB>和LaAl<SUB>11</SUB>O<SUB>18</SUB>含量为30vol%,ZrO<SUB>2</SUB>为固溶有2mol%Y<SUB>2</SUB>O<SUB>3</SUB>的ZrO<SUB>2</SUB>。 |