Low temperature-fired porcelain articles and electronic parts

摘要

An object of the invention is to provide a low temperature fired porcelain having an optimum firing temperature not higher than 1000° C. a reduced dielectric constant∈r, an improved quality coefficient and a low incidence of cracks. The invention provides a low temperature-fired porcelain comprising a barium component in a calculated amount of 10 to 64 weight percent when calculated as BaO, a silicon component in a calculated amount of 20 to 80 weight percent when calculated as SiO2, an aluminum component in a calculated amount of 0.1 to 20 weight percent when calculated as Al2O3, a boron component in a calculated amount of 0.3 to 1.0 weight percent when calculated as B2O3 a zinc component in a calculated amount of 0.5 to 20 weight percent when calculated as ZnO, and a bismuth component in a calculated amount of not higher than 20 weight percent when calculated as Bi2O3.