This invention is directed to optical cable components fabricated from an extrudable blend of high crystalline polypropylene and an impact modifying polymer to provide an enhanced balance flexural modulus, Izod notched value, grease resistance, and low shrinkage properties. The polypropylene has a crystallinity of greater than 56 weight percent and a melt flow of from 1 to 20 grams per 10 minutes at 230 degree C. At 23 degrees C, the composition yields an extrudant having a 1-percent secant modulus of at least 1,600 MPa and a notched Izod of at least 35 J/m. The composition also yields an extrud ed tube having a shrinkage of less than 2.0 percent after 24 hours at 100 degre es C. One example of the impact modifying polymer is an ethylene/1-octene polyethylene copolymer.
|
申请人 |
DOW GLOBAL TECHNOLOGIES INC. |
发明人 |
WASSERMAN, SCOTT HANLEY;ROZENBLAT, BENJAMIN R.;BUNKER, SHANA P.;WHETTEN, ALAN R.;HARE, MARIE L.;PANG, KAWAI PETER;BROWN, GEOFFREY DAVID |