The present invention is a green soda-lime-silica glass composition. The composition comprises 68 to 75% SiO2, 10 to 18% Na2O, 5 to 15% CaO, 0 to 10% MgO, 0 to 5% Al2O3, and 0 to 5% K20, where CaO+MgO is 6 to 15% and Na2O+K20 is 10 to 20%, and colorants comprising: 0.3 to 0.8 wt. % total iron as Fe2O3 wherein the ratio of FeO/total Fe as Fe2O3 is 0.35 to 0.62; 0.05 to 0.5 wt. % manganese compound as MnO2; 0 to 0.1 wt. % titanium oxide as TiO2; and 0 to 1 wt. % cerium oxide as CeO2. The colored glass has the following spectral properties at 4.0 mm. thickness: 65 to 81% light transmittance using Illuminant A (LTA) and using Illuminant C has a dominant wavelength of 494 to 555 nanometers with an excitation purity of 2 to 9%.
|