| 摘要 |
<p>A transparent heat-swellable material, a method for its preparation and fire-resistant glazing panels in which it is incorporated, are provided by a mixture of hydrated alkali metal silicate and an additive selected from polyalcohols and mono-or polysaccharides, in which the additive content is in the range of 5 to 22% by weight, the water content is in the range of 12 to 19.5% by weight, and the hydrated alkali metal silicate has a silicon oxide (SiO2): alkali metal oxide molar ratio greater than 3.3 to 1. Glazing panels including the said material offer thermal insulation of greater than 30 minutes, a barrier to flames and fumes for greater than 90 minutes and thermal radiation of less than 10 kW/m2, or even of less than 6 kW/m2, after 90 minutes.</p> |