| 摘要 |
A method for fabricating composite light-weighted glass ceramics, suitable for use as, e.g. mirror blanks or microlithography stages, at low temperatures is disclosed. Component pieces are polished then joined at low temperature using a silicate-containing joining liquid. Assembly is then performed in such a way that the joining liquid forms an interface between each component. After a period of low or slightly elevated temperature curing, rigid joints are formed throughout and the composite is dimensionally, vibrationally, and temperature stable and can withstand tensile stresses >4000 psi. The room-temperature cured composite can be heat treated using a slow, systematic temperature increase to dehydrate the joints. A sealing coating may optionally be provided to prevent excess dried joining liquid from flaking off the formed joint. |