| 摘要 |
<p>A pressure-sensitive adhesive sheet prepared by coating a composition containing a) 100 parts by weight of monomers composed of from 70 to 100% by weight of a (meth) acrylic acid alkyl ester, said alkyl group having from 2 to 14 carbon atoms, and from 0 to 30% by weight of a monoethylenically unsaturated monomer copolymerizing therewith, b) from 0.1 to 5 parts by weight of a radical chain inhibitor, c) from 0.02 to 5 parts by weight of a polyfunctional (meth)acrylate as a crosslinking agent, d) from 0.005 to 1 part by weight of a photopolymerization initiator, and e) from 0.01 to 10 parts by weight of a silane coupling agent, on a releasing-treated film having a good surface smoothness and photopolymerizing the coated layer to form a pressure-sensitive adhesive layer having a haze value of 1% or lower and a total light transmission of at least 90%. The pressure-sensitive adhesive sheet is excellent in the transparency, the foaming resistance, the low out-gas property, and the discoloring resistance (heat resistance and weather resistance).</p> |