The present invention relates to a process for preparation of polyolefin/inorganic component nanocomposite by in-situ polymerization, in which, a clay is first organically modified and then silica or titanium dioxide nanometer particles are incorporated into the layers of crystal sheets of the clay by sol-gel method. And a metallocene catalyst is then loaded on the above-mentioned material and a finished catalyst is obtained. The said catalyst is used for in-situ polymerization of ethylene or propylene, and polyolefin/clay nanocomposite is finally obtained. The process for preparation of the catalyst according to the present invention is simple, and the mechanical properties of the nanocomposite are high. For example, the Young's modulus and the tensile strength thereof are in the ranges of 700-2600 Mpa, and 20-55 MPa respectively.
|