摘要 |
Preparation is made of alloy powder comprising 3.0-8.0 wt % Si, 0.1-1.0 wt % O, 0-2.0 wt % (0 being exclusive) of at least one element selected from Mn, Al, V, Cr, and Ti, and balance Fe and having a particle size substantially equal to 150 mum or less. A binder is mixed with the alloy powder to form a mixture. The mixture is compaction-formed by the use of a die. Thus, a powder core is obtained which has a 20 kHz a.c. permeability equal to 20 or more under an applied d.c. magnetic field of 12000 A/m, a core loss characteristic of 1000 kW/m<3 >under the conditions of 20 kHz and 0.1 T, saturation magnetization of 10000 G or more, and coercive force of 3.0 Oe or less.
|