| 摘要 |
The present invention provides a carburizing method that involves heating a steel component quickly to a relatively high carburizing temperature (e.g. 1900 degrees F. and above), contacting the component at the relatively high carburizing temperature with a methane-containing carburization atmosphere for time to form a carbon-enriched surface case on the component, and cooling the component at a relatively slow rate effective to provide a relatively soft martensite-free surface case on the component. The component then is subjected to a hardening treatment wherein the carburized component is heated to a hardening temperature in the austenitic range followed by quenching and tempering to form a tempered martensitic surface case on an underlying non-martenistic core.
|