The invention concerns a method for making aluminium alloy strips containing (by weight) at least 0.15 to 1.5% Fe and/or 0.35 to 1.9% Mn, with Fe+Mn<2.5% and optionally Si<0.8%, Mg<0.2%, Cu<0.2%, Cr<0.2%, Zn<0.2%, and other elements each <0.1% and <0.3 % in all, by continuous casting between two cylinders cooled and shrinked to a thickness ranging between 1 and 5 mm, the force applied to the cylinders during casting, expressed in tonnes per meter of strip width, being less than 300+2000/e, e being the cast strip thickness in mm. The invention also concerns strips in alloy of the same composition, twin-roll cast between 1 and 5 mm thick and having a product R0.2 (MPa)xA (%) greater than 2500, and preferably than 3000.
|