PCT No. PCT/DK94/00304 Sec. 371 Date Feb. 20, 1996 Sec. 102(e) Date Feb. 20, 1996 PCT Filed Aug. 12, 1994 PCT Pub. No. WO95/05685 PCT Pub. Date Feb. 23, 1995Vanadium doping has been found to increase the sinterability of LaxCayCrO3 (x+y=1) while retaining its high temperature electrical and chemical properties. Specimens of LaxCayCrO3 with about 2 mol % V were sintered at 1,300 DEG to 1,450 DEG C. for 2 to 8 hours to achieve more than 92% theoretical density, as compared to less than 75% for those specimens not containing V. The electrical conductivity of La0,76Ca0,26 CrO3+2 mol % V in 10-16 and 1 atm of O2, was measured to be 12 and 30 S/cm, respectively. Preliminary experiments with tape cast laminates and spray coated specimens give indication that LaxCayCrO3+V can be sintered on YSZ with good adherence between the two materials. |