| 摘要 |
A sintered alloy for valve seats is comprised of carbon at 1 to 2 percent by weight, chromium at 3.5 to 4.7 percent by weight, molybdenum at 4.5 to 6.5 percent by weight, tungsten at 5.2 to 7.0 percent by weight, vanadium at 1.5 to 3.2 percent by weight, and the remainder of iron and unavoidable impurities. Enstatite particles at 1 to 3 percent by weight, hard alloy particles (A) with a Vickers hardness of 500 to 900 at 15 to 25 percent by weight, and hard alloy particles (B) with a Vickers hardness of 1000 or more at 5 to 15 percent by weight (A+B=35 percent by weight or less) are dispersed in the matrix of the sintered alloy skeleton distributed with carbide. Copper or copper alloy at 15 to 20 percent by weight is infiltrated into pores of the skeleton.
|