SiC Fiber-reinforced SiC-matrix composite and manufacturing method thereof

摘要

SiC fiber-reinforced SiC-matrix composite has the structure that SiC filaments are inserted into SiC matrix formed as a pyrolysis product of polyvinyl-silane (PVS) infiltrated into openings of said SiC filaments. PVS as a polymeric SiC precursor has structural units (a) and (b) at an a/b ratio of 1. A SiC fiber preform is impregnated with PVS slurry in an open or vacuum atmosphere, preheated at 300-400° C. in an inert gas atmosphere to moderate PVS to a viscous or semi-cured state, and then pyrolyzed in an argon atmosphere under application of a unidirectional pressure. A product is SiC fiber-reinforced SiC-matrix composite excellent in mechanical strength and high-temperature property with high density. The SiC composite is further densified by infiltration of PVS slurry suspending fine SiC particles therein or by repetition of impregnation with sole PVS and pressure-less pyrolysis after the pressurized pyrolysis. (a) -SiH2-CH2-CH2-