| 摘要 |
<p>A method of joining metal and ceramic parts, wherein an alumina forming metal part and a ceramic part are provided. A braze material in placed between the alumina forming metal part and the ceramic part, and the combination is then heated in an oxidizing atmosphere, preferably in air at a temperature of between 500 °C and 1300 °C. The alumina forming metal parts are selected from the group consisting of high temperature stainless steels, such as Durafoil (alpha-4), Fecralloy, Alumina-coated 430 stainless steel and Crofer-22APU, and high temperature superalloys such as Haynes 214, Nicrofer 6025, and Ducraloy. The braze material is selected as a metal oxide-noble metal mixture, preferably AG-CuO, Ag-V2O5, and Pt-Nb2O5, and more preferably between 30.65 to 100 mole% Ag in CuO.</p> |