| 摘要 |
Low silicon sodium X zeolite containing little or no sodium A zeolite as by-product, is prepared by direct synthesis from sodium ion-containing hydrogels, the crystallization step being carried out by maintaining the hydrogels at a temperature below about 70° C., and preferably in the range of about 50 to about 70° C. for the duration of the crystallization step. Preferably, the ratios of components in the solutions used to make the hydrogel are such that in the hydrogel the silica/alumina molar ratio will be in the range of about 2.25:1 to about 2.4:1; the sodium oxide to silica molar ratio will be in the range 1.6:1 to about 1.9:1; and the water to sodium oxide molar ratio will be greater than about 60:1.
|