<p>The present invention relates to an ultra-high strength cold rolled steel sheet having 880 to 1170 MPa of tensile strength, that consists essentially of 0.01 to 0.07% C, 0.3% or less Si, 0.1% or less P, 0.01% or less S, 0.01 to 0.1% sol.Al, 0.0050% or less N, 1.6 to 2.5% of sum of at least one element selected from the group consisting of Mn, Cr, and Mo, by mass, and balance of Fe, and that has an inner zone deeper than 10 µm from the surface of the steel sheet being substantially martensitic single phase structure. Since the steel sheet has hole expansion ratio of 75% or more, specified by the Standard of Japan Iron and Steel Federation, JFST1001-1996, tensile strength in a range of from 880 to 1170 MPa, and excellent mechanically joining property, it is suitable for automobile seat frames.</p> |