摘要

An electrically insulating composition for bonding to metal and method for applying the composition in sheet form. The insulating composition comprises a polyolefin polymer adapted for elevated temperature crosslinking and a co-bonding agent mixed with the polyolefin polymer in an amount up to about 60 parts of tile co-bonding agent to 100 parts of the polyolefin polymer. Preferably, the insulating composition cures in contact with metal pre-heated to elevated temperatures in a range from about 140° C. to about 190° C. to provide a lap-shear bond strength between the electrically insulating composition and a metal substrate of from about 3.3 MPa to about 12 MPa.