Heat treatment process for steel comprises carbonitriding the steel surface, adjusting austenitic temperature, quenching, isothermally converting until specified residual austenite is present in core of component, and cooling |
摘要 |
Heat treatment process comprises carbonitriding on steel surface at 860-930 deg C in atmosphere containing 0.6-1.3% carbon, up to 20% ammonia, up to 1.1% carbon and nitrogen; adjusting austenitic temperature to 830-860 deg C; quenching at 190-230 deg C; isothermally converting at 190-230 deg C for several hours until residual austenite in component core is less than 5%; and cooling to room temperature.
|