摘要 |
A steel sheet for disk brake with improved anti-warp property has a chemical composition comprising, in mass percent, 0.05 - 0.15% of C, not more than 1.0% of Si, not more than 2.0% of Mn, not more than 1.0% of Ni, 9.0 - 15.0% of Cr, 0.5 - 4.0% of Cu, 0.10 - 2.0% of Mo, not more than 0.10% of N, 0.05 - 1.0% of Nb, and the balance of Fe and unavoidable impurities and having a gamma max value defined by: <DF> gamma max = 420C + 470N + 23Ni + 7Mn + 9Cu - 11.5Cr - 11.5Si - 12Mo - 3.5Nb + 189 </DF> of not greater than 80. A brake disk obtained from the steel sheet keeps disk periphery warp height within 0.3 mm when the disk is subjected to 500 cycles of repeated heating/cooling each consisting of ÄTemperature increase at a rate of 5 - 20 DEG C/sec up to 600 DEG C => Maintaining at 600 DEG C during 10 sec => Water coolingÜ. |