Physically foamed fine cellular polyethylene foam

摘要

The invention relates to continuously extruded physically foamed fine cellular polyethylene foam having a structure in which more than 95 % of the cells have a cell diameter smaller than 150 micrometers. The density is between 10 and 100 kg/m<3>. The invention also relates to a process for physical foaming polyethylene in the presence of a nucleating agent. The nucleating agent is an organic compound which, on changing to the solid phase, forms crystals and which in its melt phase is soluble in the molten polyethylene. The difference in crystallization temperature between the polyethylene and the nucleating agent is greater than 10 DEG C. The difference between the melting temperature and the crystallization temperature of the nucleating agent is less than 20 DEG C.