Porous alumina fabrication procedures

摘要

This invention relates to a method of producing an alumina porous material using a mixed powder of alumina powder and aluminum hydroxide represented by the chemical formula Al(OH)3 at different percentages as the starting material, comprising the steps of heating this mixed powder to decompose the aluminum hydroxide and further heat treating it within a temperature range of 1,000 to 1,600° C., and to the alumina porous material produced by the above-mentioned method with a porosity exceeding 40 volume % and its specific surface area of 8 to 40 m2/g, and further to a filter and catalyst carrier that are obtained using this alumina porous material.