TITANIUM ALLOY AND METHOD FOR HEAT TREATMENT OF LARGE-SIZED SEMIFINISHED MATERIALS OF SAID ALLOY

摘要

The inventive titanium alloy comprises, expressed in mass %; aluminium 4.0-6.0; vanadium 4.5-5.0; molybdenum 4.5-5.0; chromium 2.0-3.6; ferrum 0.2-0.5; the rest being titanium. An equivalent molybdenum content is determined as corresponding to Mo equiv.>/= 13.8. The total aluminium and zirconium content does not exceed 7.2. The inventive method for heat treatment consists in heating to t beta <> alpha + beta -(30-70) DEG C, conditioning during 2-5 hrs. at that temperature, air or water cooling and age-hardening at a temperature ranging from 540 DEG C to 600 DEG C during 8-16 hrs. Said alloy has a high volumetric deformability and is used for manufacturing massive large-sized forged and pressed pieces having a high strength level, satisfactory characteristics of plasticity and fracture toughness.