An amorphous Zr alloy has a composition expressed as Zr-Ala-Nib-Cuc-Md. M is one or more elements selected from Ti, Nb and Pd. The a, b, c, and d are amounts in atomic %, and satisfy the following formulas. 5<=a<=0; 30<=b+c<=50; b/c<=1/3; and 0<d<=7. The remainder are Zr and inevitable impurities. The alloy contains a non-crystalline phase of 90% or higher by volume. Also, the amorphous alloy indicates an excellent glass-forming ability with a supercooled liquid range over 100° C. (indicated by a difference between the crystallization temperature and the glass transition temperature) and which has a thickness of 1 mm or thicker. Further, it has excellent strength and toughness indicated by the following mechanical characteristics: tensile strength of 1800 MPa or higher; flexural strength of 2500 MPa or higher; Charpy impact value of 100 kJ/m2 or higher; and fracture toughness value of 50 MPa*m1/2 or higher.
|